Fortis AD822 - Ultra Clear

Ultra Clear high build epoxy resin

Description

Fortis AD822 Ultra Clear is solvent free, liquid epoxy resin system specifically designed for applications that require a crystal clear, high gloss casting that will cure at room temperature. AD822 Ultra Clear is a low viscosity epoxy allowing superior air release for a bubble free finish, and is designed for medium sized castings between 5 and 30mm in a single pour. Multiple pours can be used for river table applications.

Material

2 Component Epoxy

Advantages

• Low viscosity
• Excellent bubble release
• Self levelling
• Low exotherm
• High clarity and low colour

Industries

Construction, Furniture & Woodworking, Concrete Repair, Industrial & Mining

Applications

Cover working area with cardboard or plastic. The surface to be coated should be dry and free of contaminants. For best results, apply at temperatures between 15 and 30ºC and at below 85% humidity. Air bubbles may form on the surface. Air bubbe release is greatly enhanced by use of a heat gun or gas torch. Care should be taken to avoid over heating in one spot – sweep the heat gun continuously across the surface for a few seconds. The mixed product should be cured in a warm, dust free area, and should be covered with a box. For pourous substrates it is best to brush and seal the surface prior to casting resin.

MIXING

Ensure Fortis AD 822 Ultra Clear Part A and B are shaken prior to pouring and mixing. Graduated plastic mixing containers are recommended for measuring volumetric quantities. Part B is to be added to Part A and mixed at low speed with a Jiffy style mechanical mixer. Mix only enough material for immediate use. Care should be taken to minimize air introduced during mixing. Mix until a smooth and homogeneous mixture is formed, free of striations. This should take approximately 3 minutes. Ensure material from the bottom and edges of the pail are sufficiently mixed. Let material stand for 1 minute. Mix for an additional minute.

MIXING VOLUME

The cure speed of this product depends greatly upon the volume of product mixed. If mixing large volumes, material should be poured quickly into the desired cast. Material left to stand in bulk areas such as mixing containers will exotherm and react quickly. 1L of mixed material will exotherm excessively after approximately 1 hour and will need to be split into smaller volumes. Material cast into a 400mL block 80mm high and 40mm in diameter will exotherm to greater than 120ºC and discolour.

Surfaces

Working area should be covered with cardboard or plastic. The surface to be coated should be dry and free of contaminants. Ensure all pourous substrates have been precoated with a thin coat of 822 Clear to prevent air blow out.

Feature
Specification
Color
Clear Liquid
Pot life (100g at 25 ºC)
60min
Thin film set time (at 25 ºC)
24 hours
Cured to solid state
7 Days
Cure to maximum strength
7 Days
Shore D hardness (at 20 ºC)
80